Bonding pastes play an important role by acting as a complement for the production of FRP products in composite industry. Besides fibrous and non-fibrous bonding pastes İlkalem also produces space-filling type and lightweight providing type products. Further details regarding our products are indicated for your convenience.
| TK-501BP | High performance fiberglass reinforced bonding paste |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | |
|---|---|---|---|
| High bonding characteristic of GRP parts | Bonding of boats and sea vehicles | Chemical base | Orthophthalic |
| Micronized fiberglass reinforced | Bonding of car, bus and truck body parts | Application | Hand lay-up Spatula |
| Has structural flexibility | Bonding of many GRP parts | Viscosity (cps) | 120000 – 150000 |
| Thixotropy | Yes | ||
| Density(g/cm³) | 1,25 – 1,35 | ||
| Monomer content (%) | 22 – 24 | ||
| Gel time (min) | 15 – 20 (*) | ||
| Exothermic peak (°C) | 90 – 120 (*) | ||
| Curing system (*) | 1% MEK P, preaccelerated | ||
| TIX-081 | Fiberglass reinforced liquid laminate bonding paste |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | |
|---|---|---|---|
| Micronized fiberglass reinforced | For the purpose of filling the rear parts offiberglass facing adhesion problems on curved and zigzag sections | Chemical base | Orthophthalic |
| Helps to ensure that the fiberglass lies tightly during lamination | For the prevention of fiberglass sliding | Application | Brush Spatula |
| Has structural flexibility | Viscosity (cps) | 40000 – 50000 | |
| Thixotropy | Yes | ||
| Density(g/cm³) | 1,20 – 1,30 | ||
| Monomer content (%) | 13 – 15 | ||
| Gel time (min) | 20 – 30 (*) | ||
| Exothermic peak (°C) | 80– 100(*) | ||
| Curing system (*) | 2% MEK P, pre-accelerated | ||
| G-TIX | Rigid bonding paste-standard |