Casting Type

In this group of resins high filler capacity type resins take place besides transparent casting types. Especially appropriate for the production of bath tubs, shower trays, wash basins, closets, bathroom/kitchen sinks and floor tiles.

P-068 ORTHO unsaturated polyester resin for casting applications
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Low volumetric shrinkage Sanitary materials such as kitchen top,
kitchen sink and bath tub
Chemical base                Orthophthalic Tensile strength (MPa) 50 – 60  
High filler capacity Artificial marble Application Casting Tensile elongation (%)  2 – 3 
  Electrical pannels Viscosity (cps) 500 – 700  Tensile E-modulus (MPa)  3000 – 4000 
  Souvenir accessories  Thixotropy No Flexural strength (MPa) 100 – 110
    Density(g/cm³)  1,11 – 1,12     Hardness (barcol) 34 – 36 
    Monomer content (%) 34 – 36    Heat distortion temperature(°C) 50 – 53
    Acid value (mgKOH/g) 18 – 30  Water absorption (mg) 49 – 51
     Gel time (min) 8 – 12 (*)    
    Exothermic peak (°C)  160 – 170 (*)     
    Curing system (*) 1% Co(1%) + 1% MEK P    (**) Test applied after post cure application  
P-060 ORTHO unsaturated polyester resin for casting applications
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Low volumetric shrinkage Sanitary materials such as kitchen top,
kitchen sink and bath tub
Chemical base                Orthophthalic Tensile strength (MPa) 45 – 55 
High filler capacity Artificial marble Application Casting Tensile elongation (%) 1,5 – 2,5 
Perfect surface quality Souvenir accessories  Viscosity (cps) 900 – 1100  Tensile E-modulus (MPa) 3000-4000 
    Thixotropy No Flexural strength (MPa)   75 – 85
    Density(g/cm³)  1,11 – 1,12     Hardness (GYZJ 934-1) 38 - 40
    Monomer content (%) 34 – 36    Heat distortion temperature (°C) 58 -  60
    Acid value (mgKOH/g) 18 – 30  Water absorption (mg) 39 – 41
     Gel time (min) 7 – 10 (*)    
    Exothermic peak (°C)  160 – 170 (*)     
    Curing system (*) 1% Co(1%) + 1% MEK P    (**) Test applied after post cure application  
P-053 ORTHO unsaturated polyester resin for casting applications
P-6817 ORTHO unsaturated polyester resin for casting applications
P-104 ORTHO unsaturated polyester resin for transparent casting applications
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Medium reactivity  Transparent casting materials in small sizes
(trinkets, small figurines, key chains)
Chemical base Orthophthalic Tensile strength (MPa) 50 – 60 
Low volumetric shrinkage Souvenir accessories Application Casting Tensile elongation (%) 1 – 2
    Viscosity (cps)  700 – 900  Tensile E-modulus (MPa) 3000 – 4000  
    Thixotropy No Flexural strength (MPa) 70 – 80
    Density(g/cm³)  1,11 – 1,13  Hardness (GYZJ 934-1) 40 – 42 
    Monomer content (%) 33 – 35  Heat distortion temperature (°C) 76 – 79  
    Acid value (mgKOH/g) 18 – 30  Water absorption (mg) 39 – 41
    Gel time (min) 8 – 12 (*)      
    Exothermic peak (°C) 170 – 180 (*)    
    Curing system (*) 1% Co(1%) + 1% MEK P (**) Test applied after post cure application