Button Type

This group of polyester resins are designed for textile sector purposing centrifugal sheet type casting and rod type casting. For coloring Ilkester pigment pastes are appropriate products.

P-104D ORTHO unsaturated polyester resin for centrifugal casting of button
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Excellent compatibility with pearl,
opaque and transparent pigment pastes
Button production in different sizes Chemical base Orthophthalic Tensile strength (MPa) 60 – 70
Cured buttons have color stability   Application Centrifugal casting Tensile elongation (%) 2 – 3
Cured buttons have  uniform flawless gloss   Viscosity (cps) 700 - 900 Tensile E-modulus (MPa) 3000-4000
High impact resistance   Thixotropy No Flexural strength (MPa) 100 – 110 
Does not contain heavy metal and phthalate   Density(g/cm³)   1,12 – 1,14    Hardness (GYZJ 934-1) 34 – 36 
    Monomer content (%) 32 – 34  Heat distortion temperature (°C) 51 – 54
    Acid value (mgKOH/g) 18 – 35  Water absorption (mg) 55 - 57
    Gel time (min) 7 – 11 (*)    
    Exothermic peak (°C) 145 – 165 (*)    
    Curing system (*) 0,6% Co(1%) + 1% MEK P    (**) Test applied after post cure application  

 

P-405D ORTHO unsaturated polyester resin for centrifugal casting of button
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Excellent compatibility with pearl, opaque
and transparent pigment pastes
Button production in different sizes Chemical base Orthophthalic Tensile strength (MPa) 60 – 70
Cured buttons have color stability   Application Centrifugal casting Tensile elongation (%) 2 – 3
 Cured buttons have uniform flawless gloss   Viscosity (cps) 700 – 900   Tensile E-modulus (MPa) 2500 – 3500 
Does not contain heavy metal and phthalate   Thixotropy No Flexural strength (MPa) 110 – 120   
    Density(g/cm³)  1,11 – 1,13      Hardness (GYZJ 934-1) 34 – 36 
    Monomer content (%) 30 – 32   Heat distortion temperature (C) 57 – 60
    Acid value (mgKOH/g) 18 – 25  Water absorption (mg) 57 – 59
    Gel time (min) 7 – 11 (*)    
    Exothermic peak (°C) 160 – 180 (*)    
    Curing system (*) 1% Co(1%) + 1% MEK P    (**) Test applied after post cure application  

 

P-128D ORTHO unsaturated polyester resin for centrifugal casting of button
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Excellent compatibility with pearl, opaque
and transparent pigment pastes
Button production in different sizes Chemical base Orthophthalic Tensile strength (MPa) 65 – 75
Contains special blue color for excellent whiteness   Application Centrifugal casting Tensile elongation (%) 1,5 – 2,5
Does not contain heavy metal and phthalate    Viscosity (cps) 1000 – 1200  Tensile E-modulus (MPa) 2500 – 3500 
    Thixotropy No Flexural strength (MPa) 140 – 150  
    Density(g/cm³)   1,12 – 1,14    Hardness (GYZJ 934-1) 34 – 36 
    Monomer content (%) 28 – 30  Heat distortion temperature (°C) 51 – 54
    Acid value (mgKOH/g) 18 – 35  Water absorption (mg) 52 – 54 
    Gel time (min) 7 – 11 (*)    
    Exothermic peak (°C) 155 – 175 (*)    
    Curing system (*) 0,6% Co(1%) + 1% MEK P    (**) Test applied after post cure application  

 

P-1004D ORTHO thixotropic unsaturated polyester resin for rod casting of button
PROPERTIES FIELD OF APPLICATION TECHNICAL PROPERTIES MECHANICAL PROPERTIES(**)
Excellent compatibility with pearl,
opaque and transparent pigment pastes
Button production in different sizes Chemical base Orthophthalic Tensile strength (MPa) 55 – 65
Cured buttons have color stability   Application Rod casting Tensile elongation (%) 1 – 2
Cured buttons have  uniform flowless gloss   Viscosity (cps) 1500 – 2000   Tensile E-modulus (MPa) 3500 – 4500 
High impact resistance   Thixotropy Yes Flexural strength (MPa) 90– 100
Does not contain heavy metal and phthalate   Density(gr/cm³)  1,12 – 1,14        Hardness (GYZJ 934-1) 40– 42
Provides button production without wasting risk   Monomer content (%) 30 – 32   Heat distortion temperature (°C) 58 – 61
    Acid value (mgKOH/g) 18– 35 Water absorption (mg) 47 – 49 
    Gel time (min) 8 – 11 (*)    
    Exothermic peak (°C) 145 – 165 (*)    
    Curing system (*) 0,6% Co(1%) + 1% MEK P    (**) Test applied after post cure application  

 

P-1006D ORTHO thixotropic unsaturated polyester resin for rod casting of button
P-4004D ORTHO thixotropic unsaturated polyester resin for rod casting of button