This group of gelcoats are extremely high chemical and mechanical resistancy, resistant to toug atmospheric conditions (water, UV, temperature). Water and chemical resistant this group of gelcoats are used in marine, aquapark, automotive, energy and construction industry for producing sea vessels, water slides, swimming pools, sanitary materials, modular cabins, etc. Keeping the appearance under heavy atmospheric conditions, non-cracking performance due to the structural character and high resistancy to friction are the main features of these gelcoats.Our brush and spray type gelcoats taking place in this group provide perfect results with İlkester high performance pigment pastes. Due to their super quality highly preffered fort he consumption in aquapark, water slides productions, automotive and marine sectors. Before dispatching to final consumers, colored high performance gelcoats are tested by İlkalem R&D regarding temperature, water, UV and chemical resistancy.
| GIN-913 S | ISO/NPG acrylic modified gelcoat- spray up |
| GIN-913 B | ISO/NPG acrylic modified gelcoat- brush |
| GIN-915 S | ISO/NPG acrylic modified marine gelcoat- spray up |
| GIN-915 B | ISO/NPG acrylic modified marine gelcoat- brush |
| GİN-4013 | ISO/NPG acrylic modified gelcoat- spray up |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Used as finished gelcoat | Equipments for pools and waterparks | Chemical base | Isophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| Maximum UV resistance | Boats and other sea vehicles | Application | Spray-up | Tensile elongation (%) | 1,5 – 2,5 |
| High glossy surface | Car, bus and truck body parts | Viscosity (cps) | 2000 – 4000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| High chemical resistance | Sanitary materials such as kitchen top, kitchensink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| Ultimate resistance to atmospheric medium | Military and defense industry applications | Density(g/cm³) | 1,09 – 1,11 | Hardness (GYZJ 934-1) | 30 - 40 |
| High resistance to hydrolysis | City furniture and surface coverings | Monomer content (%) | 41 – 45 | Heat distortion temperature (°C) | 95 – 97 |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 30 – 35 | ||
| Exothermic peak (°C) | 200 – 220 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GİN-3013 | ISO/NPG acrylic modified gelcoat- brush |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Used as finished gelcoat | Equipments for pools and waterparks | Chemical base | Isophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| Maximum UV resistance | Boats and other sea vehicles | Application | Brush Roller |
Tensile elongation (%) | 1,5 – 2,5 |
| High glossy surface | Car, bus and truck body parts | Viscosity (cps) | 8000 – 10000 | Tensile E-modulus (MPa) | 4000 – 4500 |
| High chemical resistance | Sanitary materials such as kitchen top,kitchen sink, bath tub |
Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| Ultimate resistance to atmospheric medium | Military and defense industry applications | Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 30 - 40 |
| High resistance to hydrolysis | City furniture and surface coverings | Monomer content (%) | 32 – 36 | Heat distortion temperature (°C) | 95 – 97 |
| Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 30 – 35 | ||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GİN-413 | ISO/NPG acrylic modified gelcoat- spray up |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Used as finished gelcoat | Equipments for pools and waterparks | Chemical base | Isophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| Excellent resistance to cracking due to structural flexibility | Boats and other sea vehicles | Application | Spray-up | Tensile elongation (%) | 2 – 2,5 |
| Maximum UV resistance | Car, bus and truck body parts | Viscosity (cps) | 2000 – 4000 | Tensile E-modulus (MPa) | 3000 – 3500 |
| High glossy surface | Sanitary materials such as kitchen top,kitchen sink, bath tub | Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| High chemical resistance | Military and defense industry applications | Density(gr/cm³) | 1,09 – 1,10 | Hardness (GYZJ 934-1) | 30 - 40 |
| Ultimate resistance to atmospheric medium | City furniture and surface coverings | Monomer content (%) | 39 – 43 | Heat distortion temperature (°C) | 83 – 87 |
| High resistance to hydrolysis | Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 40 – 42 | |
| Exothermic peak (°C) | 200 – 220 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors
| GİN-313 | ISO/NPG acrylic modified gelcoat- brush |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Used as finished gelcoat | Equipments for pools and waterparks | Chemical base | Isophthalic/NPG | Tensile strength (MPa) | 60 – 70 |
| Excellent resistance to cracking due to structural flexibility |
Boats and other sea vehicles | Application | Brush/Roller | Tensile elongation (%) | 2 – 2,5 |
| Maximum UV resistance | Car, bus and truck body parts | Viscosity (cps) | 8000 – 10000 | Tensile E-modulus (MPa) | 3500 – 3500 |
| High glossy surface | Sanitary materials such as kitchen top,kitchen sink, bath tub | Thixotropy | Yes | Flexural strength (MPa) | 110 – 120 |
| High chemical resistance | Military and defense industry applications | Density(g/cm³) | 1,11 – 1,13 | Hardness (GYZJ 934-1) | 35 - 40 |
| Ultimate resistance to atmospheric medium | City furniture and surface coverings | Monomer content (%) | 34– 38 | Heat distortion temperature (°C) | 83 – 85 |
| High resistance to hydrolysis | Gel time (min) | 10 – 20 (*) | Water absorption (mg) | 40 – 45 | |
| Exothermic peak (°C) | 165 – 195 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | ||||
| (**) Test applied as polyester after post cure application | |||||
Comments
Available in desired colors