| PM-220 | ORTHO abrasive type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | |||
|---|---|---|---|---|---|---|
| Used for the production of abrasive stones | Natural marble abrasion and surface wiping with the abrasive stones |
Chemical base | Orthophthalic | Tensile strength (MPa) | 60 – 70 | |
| Amine accelerated | Application | Filled casting | Tensile elongation (%) | 1 – 2 | ||
| Has flexible structure and paraffin free | Viscosity (cps) | 500 – 600 | Tensile E-modulus (MPa) | 4000 – 5000 | ||
| Shelf life of at least one year | Thixotropy | No | Flexural strength (MPa) | 80 – 90 | ||
| Density(gr/cm3) 20°C | 1,10 – 1,11 | Hardness (barcol) | 40 – 42 | |||
| Monomer content (%) | 35– 37 | Heat distortion temperature (°C) | 64 – 66 | |||
| Acid value (mgKOH/g) | 18 – 35 | Water absorption (mg) | 39 – 41 | |||
| Gel time (min) | 8 – 11 (*) | |||||
| Exothermic peak (°C) | 160 – 180 (*) | |||||
| Curing system (*) | 2% BPO paste(50%) | (**) Test applied after post cure application | ||||
| PM-245 | ORTHO polyester resin for production of adhesive paste |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Amine accelerated | Production of adhesive pastes to be used for bonding marble on marble and marble on different surfaces |
Chemical base | Orthophthalic | Tensile strength (MPa) | 50 – 60 |
| Shelf life of at least one year | Application | Adhesive paste production | Tensile elongation (%) | 1 – 2 | |
| Suitable for use in cold climate conditions | Viscosity (cps) | 650 – 750 | Tensile E-modulus (MPa) | 4000 – 5000 | |
| Thixotropy | No | Flexural strength (MPa) | 80 – 90 | ||
| Density(gr/cm3) 20°C | 1,10 – 1,11 | Hardness (GYZJ 935-1) | 40– 42 | ||
| Monomer content (%) | 36 – 38 | Heat distortion temperature (°C) | 90– 93 | ||
| Acid value (mgKOH/g) | 18 – 24 | Water absorption (mg) | 36– 38 | ||
| Gel time (min) | 8 – 12 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 3% BPO paste(50%) | (**)Test applied after post cure application | |||
| PM-246 | ORTHO polyester resin for production of adhesive paste |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Amine accelerated | Production of adhesive pastes to be used for bonding marble on marble and marble on different surfaces |
Chemical base | Orthophthalic | Tensile strength (MPa) | 50 – 60 |
| Shelf life of at least one year | Application | Adhesive paste production | Tensile elongation (%) | 1 – 2 | |
| Suitable for use in hot climate conditions | Viscosity (cps) | 650 – 750 | Tensile E-modulus (MPa) | 4000 – 5000 | |
| Thixotropy | No | Flexural strength (MPa) | 80 – 90 | ||
| Density(gr/cm3) 20°C | 1,10 – 1,11 | Hardness (barcol) | 40– 42 | ||
| Monomer content (%) | 36 – 38 | Heat distortion temperature (°C) | 90– 93 | ||
| Acid value (mgKOH/g) | 18 – 24 | Water absorption (mg) | 36– 38 | ||
| Gel time (min) | 12 – 15 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 3% BPO paste(50%) | (**)Test applied after post cure application | |||