Unsaturated polyester resin for FRP hand layup, filament winding, fiber spraying applications, having high Heat Distortion Temperature and mechanical values. Best results Best results can be achieved from the production of car, bus and truck body parts, sea vessels, aquaparks, modular cabins, construction materials, storage tanks and decorative FRP furnitures.
| P-140 | 400 | ORTHO GRP type polyester resin |
| P-140 ETPS | 401 | ORTHO thixotropic pre-accelerated low styrene emission GRP type polyester resin |
| P-423 | 402 | ORTHO high reactive GRP type polyester resin |
| P-423 TA | 403 | ORTHO thixotropic pre-accelerated high reactive GRP type polyester resin |
| P-590 | 404 | DCPD based low styrene emission GRP type polyester resin |
| P-590 TA | 405 | DCPD based thixotropic pre-accelerated low styrene emission GRP type polyester resin |
| P-192 | 200 | ORTHO GRP type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 60-70 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Filament winding |
Tensine elongation (%) | 1-2 |
| Modular cabinet | Viscosity (cps) | 550 -650 | Tensile E-modulues (MPa) | 4000-5000 | |
| Water tank | Thixotropy | No | Flexural strength (MPa) | 170-180 | |
| Decorative FRP furniture | Density (g/cm3) | 1,12 - 1,14 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 33 - 35 | Heat distortion temperature (C) | 58-61 | |
| Acid value (mgKOH/g) | 18-25 | Water absorption (mg) | 29-31 | ||
| Gel time (min) | 10-18 (*) | ||||
| Exothermic peak (C) | 160-200 (*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-192 TA | 340 | ORTHO thixotropic pre-accelerated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Cars,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 – 65 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Spray-up Filament winding |
Tensile elongation (%) | 1-2 |
| No dripping during vertical application | Modular cabinet | Thixotropy | Yes | Tensile E-modulus (MPa) | 4000-5000 |
| Water tank | Viscosity (cps) | 500 – 1000 | Flexural strength (MPa) | 140 – 150 | |
| Decorative FRP furniture | Density(g/cm3) 20°C | 1,11 – 1,12 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 38 – 40 | Heat distortion temperature (°C) | 72 – 75 | |
| Acid value (mgKOH/g) | 18-25 | Water absorption (mg) | 36 – 38 | ||
| Gel time (min) | 10-18 (*) | ||||
| Exothermic peak (°C) | 160-200 (*) | ||||
| Curing system (*) | 1% MEK-P, pre-accelerated | (**) Test applied after post cure application | |||
Comments
Can be produced as unaccelerated upon request
| P-1920 | 210 | ORTHO unsaturated polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 60-70 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Filament winding |
Tensine elongation (%) | 1-2 |
| Modular cabinet | Viscosity (cps) | 550 -650 | Tensile E-modulues (MPa) | 4000-5000 | |
| Water tank | Thixotropy | No | Flexural strength (MPa) | 170-180 | |
| Decorative FRP furniture | Density g(cm3) | 1,12 - 1,14 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 33 - 35 | Heat distortion temperature (C) | 58-61 | |
| Acid value (mgKOH/g) | 18-25 | Water absorption (mg) | 29-31 | ||
| Gel time (min) | 10-18 (*) | ||||
| Exothermic peak (C) | 160-200 (*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | ||||
| P-116 | 201 | ORTHO polyester resin for GRP applications |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55-65 |
| Highly reactive | Boats and other sea vehicles | Application | Hand lay-up Filament winding |
Tensile elongation (%) | 1-2 |
| High mechanical strength | Modular cabinet | Viscosity (cps) | 350 - 400 | Tensile E-modulus (MPa) | 4000-5000 |
| Suitable for mass production | Water tank | Thixotropy | No | Flexural strength (MPa) | 140-150 |
| Decorative FRP furniture | Density(g/cm3) 20°C | 1,10 – 1,12 | Hardness (GYZJ 934-1) | 40-42 | |
| Construction materials | Monomer content (%) | 38 - 40 | Heat distortion temperature (°C) | 72 - 75 | |
| Acid value (mgKOH/g) | 18 - 24 | Water absorption (mg) | 36 - 38 | ||
| Gel time (min) | 10 - 15 (*) | ||||
| Exothermic peak (C) | 165 - 185(*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | (**) Tests applied after post cure application | |||
| P-1016 | 204 | ORTHO thixotropic pre-accelerated polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55-65 |
| Highly reactive | Boats and other sea vehicles | Application | Hand lay-up Spray-up Filament winding |
Tensine elongation (%) | 1 - 2 |
| Highly mechanical strength | Modular cabinet | Viscosity (cps) | 750- 1100 | Tensile E-modulues (MPa) | 4000-5000 |
| Suitable for mass production | Water tank | Thixotropy | Yes | Flexural strength (MPa) | 140 - 150 |
| Decorative FRP furniture | Density(gr/cm3) | 1,10 – 1,11 | Hardness (GYZJ 934-1) | 40 - 42 | |
| Construction materials | Monomer content (%) | 39 - 41 | Heat distortion temperature (°C) | 72 - 75 | |
| Acid value (mgKOH/g) | 18 - 24 | Water absorption (mg) | 36 - 38 | ||
| Gel time (min) | 10 - 15 (*) | ||||
| Exothermic peak (°C) | 165 - 185 (*) | ||||
| Curing system (*) | 1% Co(1%)+1%MEK P | (**) Test applied after post cure application | |||
Comments
Pre-accelerated type can be produced upon request
| P-1017 ETPS | 209 | ORTHO thixotropic pre-accelerated low styrene emission GRP type polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Easy and quick fiber wetting | Car,bus and truck body parts | Chemical base | Orthophthalic | Tensile strength (MPa) | 55 - 65 |
| Low volumetric shrinkage | Boats and other sea vehicles | Application | Hand lay-up Spray-up Filament winding |
Tensine elongation (%) | 1 - 2 |
| High mechanical strength | Pool filter | Viscosity (cps) | 500 - 1000 | Tensile E-modulues (MPa) | 4000-5000 |
| No dripping during vertical application | Modular cabinet | Thixotropy | Yes | Flexural strength (MPa) | 85 - 95 |
| Accepts up to 20% fiber filling | Decorative FRP furniture | Density (g/cm 3) | 1,10 – 1,12 | Hardness (GYZJ 934-1) | 40 - 42 |
| Construction materials | Monomer content (%) | 39 - 41 | Heat distortion temperature (°C) | 67 - 70 | |
| Acid value (mgKOH/g) | 18 - 30 | Water absorption (mg) | 30 - 32 | ||
| Gel time (min) | 15 - 25 (*) | ||||
| Exothermic peak (°C) | 160 - 185 (*) | ||||
| Curing system (*) | 1% MEK P, pre-accelerated | (**) Test applied after post cure application | |||
Comments
Contains blue color MEK P indicator