| P-1020 | ORTHO high reactive polyester resin |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Used as filling material for wooden surfaces as well as finish coat after sanding and polishing |
First layer filler varnish to all wooden furniture surfaces such as table, coffee table, cabinet, door, etc |
Chemical base | Orthophthalic | Tensile strength (MPa) | 40 – 50 |
| Forms dry, smooth and silky matte surface | Application | Spray-up | Tensile elongation (%) | 1 – 2 | |
| Contains paraffin-wax | Viscosity (cps) | 80 – 100 | Tensile E-modulus (MPa) | 2000 – 3000 | |
| Having low viscosity, it can only be applied horizontal | Thixotropy | No | Flexural strength (MPa) | 70 – 80 | |
| Density(gr/cm3) 20°C | 1,06 – 1,07 | Hardness (GYZJ 934-1) | 20 – 25 | ||
| Monomer content (%) | 43 - 45 | Heat distortion temperature (°C) | 58 – 60 | ||
| Acid value (mgKOH/g) | 11– 20 | Water absorption (mg) | 33 – 35 | ||
| Gel time (min) | 12 – 16 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 2% Co(1%) + 1% MEK P | (**) Test applied after post cure application | |||
| P-1002 | Polyester resin based filler varnish |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| Highly reactive | First layer filler varnish to all wooden furniture surfaces such as table, coffee table, cabinet, door, etc |
Chemical base | Orthophthalic | Tensile strength (MPa) | 30 – 40 |
| Forms dry and smooth surface | Application | Spray-up | Tensile elongation (%) | 1 – 2 | |
| Has flexible structure and paraffin free | Viscosity (cps) | 400 – 600 | Tensile E-modulus (MPa) | 2000 – 3000 | |
| Easy to sand after hardening | Thixotropy | No | Flexural strength (MPa) | 50 – 60 | |
| No dripping during vertical application | Density(g/cm³) | 1,08 – 1,10 | Hardness (GYZJ 935-1) | 70 – 42 | |
| Monomer content (%) | 38 – 40 | Heat distortion temperature (°C) | 58 – 60 | ||
| Acid value (mgKOH/g) | 18 – 30 | Water absorption (mg) | 55 – 65 | ||
| Gel time (min) | 4 – 6 (*) | ||||
| Exothermic peak (°C) | 180 – 200 (*) | ||||
| Curing system (*) | 2% Co(6%) + 2% MEK P | (**) Test applied after post cure application | |||
| P-2002 | Polyester resin based white sealer |
| PROPERTIES | FIELD OF APPLICATION | TECHNICAL PROPERTIES | MECHANICAL PROPERTIES(**) | ||
|---|---|---|---|---|---|
| High filling capacity | First layer white sealer on MDF or wooden surfaces such as table, coffee table, cabinet, door, etc |
Chemical base | Orthophthalic | Tensile strength (MPa) | 30 – 40 |
| White color | In the application of white furniture | Application | Spray-up | Tensile elongation (%) | 1 – 2 |
| Forms dry and smooth surface | Viscosity (cps) | 3000 – 6000 | Tensile E-modulus (MPa) | 2000 – 3000 | |
| Has flexible structure and paraffin free | Thixotropy | No | Flexural strength (MPa) | 50 – 60 | |
| Easy to sand after hardening | Density(g/cm³) | 1,30– 1,40 | Hardness (GYZJ 935-1) | 70 – 72 | |
| No dripping during vertical application | Monomer content (%) | 23 - 25 | Heat distortion temperature (°C) | 58 – 60 | |
| Gel time (min) | 8 – 12 (*) | Water absorption (mg) | 55 – 65 | ||
| Exothermic peak (°C) | 140 – 160 (*) | ||||
| Curing system (*) | 2% Co(3%) + 2% MEK P | ||||
| (**) Test applied after post cure application | |||||